UV/EB Oligomer
BDT-1006
BDT-1006: Hexafunctional Thioether Dendritic Acrylate Oligomer
BDT-1006 is a dendritic acrylate with an average functionality of 6. The hyper-branched structure of BDT-1006 imparts the unique combination of low diluted viscosity with unmatched chemical and thermal resistance, which is ideal in applications where withstanding exposure to the harshest conditions is paramount. Great for high-temperature applications because thermogravimetric analysis indicates the oligomer doesn’t decompose until 377 °C.
| Neat Properties | |
|---|---|
| Property | Value |
| Viscosity cP (25ºC) | 1,500 |
| Pt-Co (APHA) Color | 15 |
| Refractive Index (25ºC) | 1.493 |
| Density, g/cm3 (25ºC) | 1.17 |
| Monomer Dilution Properties | ||||||
|---|---|---|---|---|---|---|
| Value | ||||||
| Property | I30 | I50 | TM50 | TP50 | H50 | HE30 |
| Tensile Strength (MPa [psi]) | 46.2 [6700] | 40.7 [5900] | 51.7 [7500] | 55.8 [8100] | 55.2 [8000] | 66.9 [9700] |
| Elongation (%) | 2.1 | 1.9 | 2.6 | 4.2 | 4.3 | 5.2 |
| Elastic Modulus (MPa [ksi]) | 2,689.0 [390] | 2,620.0 [380] | 2,689.0 [390] | 2,344.2 [340] | 1,999.5 [290] | 2,689.0 [390] |
| Durometer Hardness | 89D | 88D | 91D | 87D | 87D | 90D |
| Water Absorption (%) 24hrs | 0.17 | 0.12 | 0.29 | 0.33 | 0.23 | 0.59 |
| MEK Double Rubs (#) | >200 | >200 | >200 | >200 | >200 | >200 |
| Viscosity (cP) | 220 @ 25ºC | 70 @ 25ºC | 400 @ 25ºC | 90 @ 25ºC | 40 @ 25ºC | 100 @ 25ºC |
** Tensile Properties per ASTM D882 - Not Tested || Incompatible X Unable to Measure